Conversion Coatings are one of the effective ways for improving adhesion of organic coatings to metallic substrates and consequently increasing anti-corrosion performance of a fully coated system. In the current research, multi-cationic conversion coating formed from sources such as hexafluorotitanic acid, sodium molybdate, phytic acid and nickel sulphate was studied and investigated. Results obtained from electrochemical impedance spectroscopy and polarization revealed that conversion coating which formed in the presence of sodium molybdate has not appropriate polarization resistance and the reason for this weak performance investigated by field emission scanning electron microscope. Obtained results showed that in the presence of sodium molybdate, there were abundant micro-cracks on the surface of the coating. After optimizing the multicationic conversion coating, an epoxy coating applied on the surface of bare steel and conversion coated one. The results obtained from adhesion and salt-spray tests indicated that the multi-cationic conversion coating causes improvement in adhesion strength of epoxy coating to steel substrate and finally increased the anti-corrosion performance of the system

Keywords: Conversion coating, Adhesion, Corrosion, Impedance, Polarization, FE-SEM

Full-Text [PDF 1476 kb]   (167 Downloads)    

Add your comments about this article : Your username or Email:

---